product information:

Structure diagram of nano silver wire transparent conductive film (MoLink):

    Nano silver wire transparent conductive film (MoLink) Specifications:


          ◆Transparency: >90% (91-93%), independent transparency of nano silver coating: >99.9%


          ◆Square resistance: 70±10Ω/port; 50±10Ω/port; 30±10Ω/port; 16±4Ω/port (ultra low square resistance)


          ◆Haze: ≤0.9%; ≤1.1%; ≤1.2%; ≤1.5%


          ◆Color b*: 1.0±0.1


          ◆Hardness: conductive surface>2H; non-conductive surface>3H


          ◆Square resistance uniformity: <10%


          ◆Bending test: 100,000 times of bending (R=3mm), impedance change <15%


          ◆Reliability test stability: high temperature and high humidity: 70℃/90%/240hrs; high temperature storage: 80℃ 240hrs;


          ◆Heat and cold shock: -40℃(2hrs)~60℃(2hrs) 30cycles; low temperature storage: -40℃ 240hrs;


          ◆Structure: Coil/Coil

    Coating surface number (optional): single-sided coating / double-sided coating


        Coil width (optional): 500mm, 760mm, 1200mm, 1500mm


        Front protective film (optional): PE protective film, PP protective film (130℃/30 minutes)


        Back protective film (optional): PE protective film, high temperature resistant PET (160℃/60 minutes), no film (3H hardened surface)

    Nano silver wire transparent conductive film (MoLink) product advantages:


         (1) Low resistance, high transmittance and low haze;
         (2) Strong adhesion: After the dust-free cloth is soaked in alcohol, there is no change in resistance after 100 times of 1Kg wipes;
         (3) Stable performance: After long-term aging, there will be no yellowing or silver line migration;
         (4) The line width and line spacing can be less than 35μm, and the resistance is normal, and there will be no sudden rise;
         (5) Either laser etching process or yellow light etching process can be used, without etching marks;
         (6) There is no matching problem between film material and silver paste, and high and low temperature silver paste can be used;
         (7) Good resistance to flexure, suitable for touch screens with high and low curvature.

Application direction: flexible high-transparent conductive film, flexible touch, medium and large size multi-touch, mobile phone tablet, solar cell,


     Microelectronics components, smart homes, automotive electronics, smart buildings, wearable devices and many other fields.

The comparative advantages of nano silver wire transparent conductive film (MoLink) and other similar products:


(1) Compared with Metal-Mesh Film, nano silver wire transparent conductive film does not have the problem of Murray interference and can be applied to display screens of various sizes; it has higher light transmittance and more With a small bending radius, the bending resistance is quite strong.


(2) Compared with ITO film, nano silver wire transparent conductive film has the following advantages: ITO is a brittle material and is not suitable for flexible touch screens. The cost is high. Nano silver wire conductive film has better bending resistance and lower cost. In order to reduce the square resistance of the ITO film, the thickness of the conductive layer needs to be increased. At the same time, the transmittance drops sharply and the haze increases sharply. However, the conductive film of silver nanowire does not have this problem. ITO film is difficult to achieve double-sided coating. High-end products need to use GFF structure, which has poor optical performance and low yield; while nano silver wire transparent conductive film can achieve double-sided coating and double-sided conductivity, with good optical performance and high yield.